Investigation of Elemental Magnetic Moments of CoCrPt Films Using X-Ray Magnetic Circular Dichroism
2006
The elemental magnetic moments of Co and Cr in CoCrPt films were investigated using xray magnetic circular dichroism (XMCD). The spin and orbital moments of Co was calculated using the sum rules; it was found that the magnetic moment of Co in CoCrPt films was dominated by spin moment contribution. The total magnetic moment of Co was found to be lower than that of bulk Co. Further, the Cr moment was aligned anti-ferromagnetically with respect to Co, resulting in a decrease of saturation magnetization (Ms) in CoCrPt films.
Optical and magnetic properties of ZnCoO thin films synthesized by electrodeposition
2008
Ternary Zn1−xCoxO crystalline films with different compositions were grown by electrodeposition. The Co content in the final compound is linked to the initial Co/Zn ratio in the starting solution. X-ray diffraction reveals a wurtzite structure for the Zn1−xCoxO films. Transmittance spectra show two effects proportional to Co content, a redshift of the absorption edge and three absorption bands, which are both interpreted to be due to the Co incorporated into the ZnO lattice. The amount of deposited charge was used to get a precise control of the film thickness. Magnetic measurements point out that Co(II) ions are isolated from each other, and consequently the films are paramagnetic. Francis…
Surface magnetic structure investigation of a nanolaminated Mn$_2$GaC thin film using a magnetic field microscope based on Nitrogen-Vacancy centers
2021
This work presents a magnetic field imaging method based on color centers in diamond crystal applied to a thin film of a nanolaminated Mn$_2$GaC MAX phase. Magnetic properties of the surface related structures have been described around the first order transition at 214 K by performing measurements in the temperature range between 200 K and 235 K with the surface features fading out by increasing temperature above the transition temperature. The results presented here demonstrate how Nitrogen-Vacancy center based magnetic microscopy can supplement the traditionally used set of experimental techniques, giving additional information of microscopic scale magnetic field features, and allowing t…
Characterization of microscopic ferromagnetic defects in thin films using magnetic microscope based on Nitrogen-Vacancy centres
2020
In this work we present results acquired by applying magnetic field imaging technique based on Nitrogen-Vacancy centres in diamond crystal for characterization of magnetic thin films defects. We used the constructed wide-field magnetic microscope for measurements of two kinds of magnetic defects in thin films. One family of defects under study was a result of non-optimal thin film growth conditions. The magnetic field maps of several regions of the thin films created under very similar conditions to previously published research revealed microscopic impurity islands of ferromagnetic defects, that potentially could disturb the magnetic properties of the surface. The second part of the measur…